PEG for Tissue Engineering

When parts or the whole of certain tissues or organs fail, there are several options for treatment, including repair, replacement with a synthetic or natural substitute, or regeneration. The fabrication of cell scaffold with hydrogel that derived from natural polymer materials is an attractive method to be applied for the tissue engineering, but some undesirable mechanical properties and immunogenic risks of natural hydrogel is a dilemma for this kind of application. However, PEG is a promising raw material for the biomaterials as well as for the tissue engineering.

There are several advantages of PEG as the raw materials for tissue engineering among other natural materials.

Synthetic Versatility
PEG that synthesized via anionic polymerization of ethylene oxide, is a synthetic and non-biodegradable polymer that can be dissolved in water with any length. Therefore, the polymerization of PEG from ethylene oxide or ethylene glycol is easily controllable in aqueous solutions with quite narrow polydispersity. Linear PEG bears only two functional groups at the end of its chain, and commercial PEGs are available with different molecular weight and functionality. While multi-arms PEG derivatives can be prepared by ethoxylation of different cores such as pentaerythritol, hexaglycerol, or tripentaerythritol. With the versatility of PEG raw materials on the market, various PEG-based products can be manufactured for the tissue engineering applications.

Biocompatibility and Biodegradability
The biocompatibility of PEG was intensive investigated but many researchers, and all of them prove this result, and demonstrate the potential application as the cell scaffold in tissue engineering. While the PEG itself has the resistance to protein adsorption, which limits the biodegradation of PEG scaffold in tissue, the block copolymer of PEG with many biodegradable polymers, such as polylactic (PLA) and polycaprolactone (PCL), can yield a new generation of PEG copolymer that inherently possesses the biocompatibility and biodegradability. Moreover, the degradation degree can be controlled by choosing vast types of PEG copolymer.

Tunable Structure
In addition to its chemical composition, the mechanical properties of PEG-based scaffold can also be tuned. Stiffness, porosity, mechanical stability and elasticity are the properties that very crucial to evaluate the biomaterials as well as the cell scaffolds. These properties are largely correlated to the degree of crosslinking. Not only the length and the molecular weight of PEG can be manipulated during the synthesis procedures, but also the functionality of end groups can be chemically modified. At meanwhile, the types of active chemicals that react with PEG to fabricate the hydrogel or scaffold is variable. All these parameters are related to the crosslinking density that influences the mechanical properties. To be used as scaffold for tissue engineering applications, the material must provide an optimal niche for cell proliferation and differentiation, focused on cell attachment. Therefore, the modifications are used to tune this property. Overall, the tunable structure of PEG hydrogel endows assorted possibilities to it on the application of tissue engineering.

Preparation methods of PEG hydrogel for scaffold

Michael addition
The Michael addition is a facile reaction between nucleophiles and activated olefins and alkynes. The mild reaction condition, the rapid cure and high conversions under physiological environment are of great significance for biological applications such as the incorporation of bioactive macromolecules and cells.

Click Chemistry
This click reaction is highly chemo-selective and can be performed under mild conditions in aqueous buffers with a wide range of pH, indicating high applicability for site-specific reaction, and generally results in a high yield of the desired product. The crosslinking in these hydrogels is extremely high, and results in a more ideal structure leading to improved properties when compared to traditional photochemically-crosslinked PEG hydrogels.